Palisander
PHYSICAL
AND MECHANICAL PROPERTIES |
|||||
|---|---|---|---|---|---|
APPARENT
SPECIFIC WEIGHT kg/m3 DIN 52102 |
2700 |
COMPRESSIVE
STRENGTH N/mm2** (dry condition) DIN 52105 |
72 |
MODULUS
OF RUPTURE |
9.55 |
POROSITY
& WATER ACCESSIBLE POROSITY DETERMINATION Wt % DIN 52102 |
0.40 |
COMPRESSIVE
STRENGTH N/mm2** (wet condition) DIN 52105 |
61.31 |
MODULUS
OF RUPTURE |
9.27 |
ABSORPTION
COEFFICIENT Wt % DIN 52103 |
0.17 |
ABRASION
RESISTANCE mm DIN 52108 |
3.84 |
COMPRESSIVE
STRENGHT AFTER FREEZING AND THAW CYCLES N/mm2** DIN 52104 & 52105 |
62.98 |
MODULUS
ELASTICITY Gpa ASTM C-170 |
18 |
IMPACT
STRENGTH cm UNI-U 32.07.248.0 |
31 |
**1 MPa = 1 N/mm2 = 10.2 kp/cm2 |
|